电工钢硅钢片Ultra-thin series: B15AHT1000, B15AHT1200, B15AT1000, B15AT1200B15AT1500, B15AT1550, B20AHT1000, B20AHT1200, B20AT1000, B20AT1200, B20AT1500, 20WTG1200, 20WTG1500 20WTG1550 B25AHV1200 B25AHV1300, B27AHV1400, B27AV1400, B30AHV1500 B30AHV1400, B35AV1700 B35AV1800High performance series: B35AH300, B50AH300, 50AH470, 50AH600, 50AH800, B50AH470, B50AH600, B50AH800, B50AR300, B50AR600, B50AR500, B50AR350, B20AT15000.35 series: B35A200, B35A210, B35A230, B35A250, B35A270,B35A300, B35A360, B35A440, B35A550, B35AH300, B35AR300, B35AY-10.5 series: B50A250, B50A270, B50A290, B50A310, B50A350, B50A400, B50A470, B50A600, B50A700, B50A800, B50A1000, B50A13000.65 series: B65A470, B65A530, B50A600B65A700, B65A800 B65A1000, B65A1300Super thick Series: 70WK340, 75WK400, 80WK420, 85WK450, 10W800 WFC-100A, silicon steel sheet performance: A low iron loss. As an important indicator of quality, each country divides the grade by the iron loss value. The lower the iron loss, the higher the grade and the higher the quality.B. High magnetic induction strength. Under the same magnetic field, the silicon steel sheet with high magnetic sensitivity can be obtained. The volume and weight of the iron core of the motor or transformer made by it are relatively small, which can save silicon steel sheet, copper wire and insulating materials, etc.C. High stacking coefficient. The surface of the silicon steel sheet is smooth, flat and uniform in thickness, which improves the stacking coefficient of the iron core.D. Good punching property. This is more important for manufacturing small and micro motor iron cores.E. The surface has good adhesion and weldability to the insulating film.

电工钢硅钢片：本文件的符号和相应的说明见表1。表 1 符号和说明符号 单位 说明P W/kg 比总损耗，通常称为铁损P1.5/50 W/kg 磁极化强度在1.5T、云南昭通附近频率在50Hz下测得的比总损耗P1 W/kg 横向试样的比总损耗值P1.5/50 P2 W/kg 纵向试样的比总损耗值P1.5/50 T1.5/50 ％ 比总损耗P1.5/50的各向异性H A/m 磁场强度J T 磁极化强度J1000 T 磁场强度峰值为1000A/m下测得的磁极化强度峰值J2500 T 磁场强度峰值为2500A/m下测得的磁极化强度峰值J5000 T 磁场强度峰值为5000A/m下测得的磁极化强度峰值J10000 T 磁场强度峰值为10000A/m下测得的磁极化强度峰值μ0 H/m 真空中的磁导率取4?×10-7 B T 磁感应强度，B＝μ0H＋JReL MPa 下屈服强度Rm MPa 抗拉强度A ％ 断后伸长率C Ω·cm2/面或Ω·mm2/面 表面绝缘电阻系数RA Ω·cm2/片或Ω·mm2/片 层间电阻系数

电工钢硅钢片硅钢是一种硅铁合金。用硅钢轧制的片材是电工领域中应用广的软磁材料，因而硅钢片又称电工钢片。硅钢片广泛用于电动机、发电机、变压器、扼流圈、电磁机构、继电器及测量仪表中电机工业大量使用厚度为0.35～0.50mm的硅钢片,用于：中型旋转机，压缩电机，通用马达，小型精密电机，电动汽车，压缩机，通用电机，电源变压器，精密变压器，节能电机，焊机变压器，稳压器，磁性密封器，加速器用电磁铁，汽车电机等；在电信高频技术中常用0.05~0.20mm的薄带钢片,以便更有效地降低涡流损耗。热轧硅钢片厚度为0.35～0.50mm，密度为7.55～7.70g/cm3,多用于大、中、小型交、直流电动机；冷轧无取向硅钢片厚度为0.35～0.50mm，密度为7.65～7.75g/cm3，多用于大型交流发电机、电动机，大、中、小型交、直流电动机；冷轧取向硅钢片厚度为0.23mm 0.27mm 0.3mm 0.35mm，密度为7.65g/cm3,多用于电力变压器、油浸式变压器，干式变压器，电抗器、磁放大器等；冷轧取向薄带厚度为0.05～0.20mm，多用于无线电高频变压器。